The SEM microphotographs of the results of the heterocoagulation process: a mixture of PTFE latex and CTAB-stabilized MWCNT dispersion by ultrasonication, b the surface of the PTFE/CTAB-stabilized MWCNT composite particles after the growth step, and 1 wt.% MWCNT/PTFE composite particles upon the completion of the heterocoagulation process prepared with c MWCNT-COOH and d CTAB-stabilized MWCNT
Figure 3 represents the morphology of the hybrid
Figure 3a shows the simple mixture of 1 wt.%
CTAB-stabilized MWCNT with PTFE dispersions prior to the
Figure 3b shows the surface of the particles containing
1 wt.% MWCNT/CTAB in the PTFE matrix after the particle-growth
Figure 3c, d represent the morphology of the ultimate
composite particles prepared with MWCNT-COOH and MWCNT/CTAB after
the stabilization process.
In Fig. 3c, a great deal of PTFE latex particles still remains
after the heterocoagulation process due to the lack of interaction
between both negatively charged MWCNT and PTFE.
Viewing this image requires a subscription. If you are a subscriber, please log in.
This image is from the article titled "Preparation of conductive PTFE nanocomposite containing multiwalled carbon nanotube via latex heterocoagulation approach"
(from Colloid and Polymer Science), which is copyrighted by Springer-Verlag. For more information on the
copyright for this image, please refer to the full image caption and to the
The image is being made available for non-commercial purposes for subscribers to SpringerImages. For more information on what you are allowed to do with this image, please see our copyright policy.
To request permissions to use any copyrighted material, please visit the source document.
Report a copyright concern regarding this image.
Log in or register to save your favorite images and download them as high-quality PowerPoint or PDF files.
Log in or register to save your search criteria.
© Springer, part of Springer Science+Business Media.
Remote Address: 188.8.131.52 Server: 21